====== C notation ====== | ====== C notation ====== |
| |
Battery capacity in Amp-hours is written as **C**. This notation is most useful when talking about charging/discharging rates. | **Battery capacity** in Amp-hours is written as **C**. 100Ah, for example. |
| |
Note: most deep cycle manufacturer's rate capacity at C/20, due to Peukert effect. In other words, a 100Ah battery will deliver 100A with a 5A load. See table at bottom for other load levels. | C notation can also be used to describe the **relative amount of current** charging/discharging battery bank. For example a 50A load on a 100Ah bank would be C/2 (100/2 == 50).((technically C/20/2, but that form is rarely seen outside formal documents)). It may also be written as 0.5C.((decimal vs. fractional expression, can be used interchangably)) |
| |
| |
| Note: most deep cycle manufacturer's rate capacity at C/20, due to Peukert effect on lead chemistries.((Lithium doesn't not have a significant Peukert effect. Capacity measured by C/20 and by amp-counting will be nearly identical)). In other words, a 100Ah battery will deliver 100A with a 5A load. See table at bottom for other load levels. |
| |
| |
===== other than 20hr rates ===== | ===== other than 20hr rates ===== |
| |
For other than C/20 loads((flooded)): | Because of the Peukert effect, lead bank //measured// capacities are strongly affected by dicharge rate. Sample data below is for flooded lead acid. C/20 capacity is multiplied by the factor below to find projected capacity at given discharge rates. |
| |
| |